Cold galvanization against corrosion. Excellent rust-protection for all iron metals, such as car bodies, exhaust systems, gates, machines, metal housings, metal fittings, fences etc. Especially suitable for the protection of welding seams and metals which are exposed to corrosion.

High-grade zinc coating with more than 90 % zinc share in the dry film
Cathodic corrosion protection for all blank metals
Resistant to highest demands against corrosion
Highheat-resistant up to 600°C
Particularly suitable for welding seams
Ideal for all metals in outside places, which are liable to rust

Basis of the binder: Epoxyester
Colour: zinc-coloured
Smell: solvent
Degree of gloss (at measurement angle 60° acc. to DIN 67530):
matt, 5 gloss units
Depending on consistence and color of the ground:
400 ml are sufficient for approx. 1.0 to 1.5 m² at covering layer
Drying time (at 20°C, 50% relative air humidity):
Dust-dry: after approx. 10 minutes
Non-sticky: after approx. 20 minutes
Coatable: after 24 hours
Resistant to temperature: after 8 to 12 hours
The drying time depends on surrounding temperature, air humidity and thickness of the applied coat.
Temperature resistant: up to 600°C
Storage stability: 10 years if appropriate storage provided (=10° to 25°C, relative air humidity of max. 60%) Size:
aerosol cans, maximum nominal volume 400 ml
Environmentally sound: The products of MOTIP DUPLI are 100% free of heavy metals. The caps and packagings are made of recyclable material.
Disposal: Only the completely emptied cans should be put into the recycling skip or appropriate container for reclaimable refuse. Cans which are not empty should be disposed off as special refuse.
Marking/Labelling: All products made by MOTIP DUPLI comply with the actual labelling regulations according to Preparation Guideline 1999/45/EG. All aerosols correspond to TRGS 200 and TRG 300 as well as to aerosol guideline 75/324/EWG in the actually valid version.

The most DUPLI-COLOR spray paints have a so-called no-spray ring or a tamper-proof cap. This is to avoid unauthorized use. Please see the corresponding advises on the cap or on the label.
Before use, carefully read and observe the warning texts on the label!

Preparation of the ground:
The metal surface has to be blank and free from fat.
Due to the high density, the Zinc Primer has to be shaked for at least 2 minutes after you hear the noise of the mixing-balls. Otherwise the valve could block.

Shake the can vigorously for approx. 2 to 3 minutes.
Test spray at an invisible spot.
Apply several covering coats.
Spray from a distance of approx. 25 to 30 cm.
After drying (approx. 24 hours) apply primer and top coat.
Do apply just thin coats to objects, which are exposed to high heat. If necessary, re-coat with temperature-resistant lacquer (test painting).
Can be coated with itself; it is possible to apply a primer and a top-coat.

Protect the object and the surrounding area from spray mist. When painting small areas it is recommended that a piece of card is used as a mask, with a hole cut in it slightly larger than the area to be sprayed. The mask should be held 1 to 2 cm from the surface. With this method, the mainly part of the spray mist is brought under control. It recommends to mask parts not to be lacquered, to protect the surrounding against the spray mist.
The aerosol can should have room temperature.
Temperature should range between +10°C and +25°C, max. air humidity 60 %.
Store in a dry place. Protect from direct sunlight and other sources of heat. Use only during dry weather, in places protected from the wind, and in well-ventilated rooms. Follow the warning texts on the labels!